NBR 6240 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem.
NBR 6240 is a non staining, medium low mooney, and medium high acrylonitrile polymer designed to aid in processing operations such as extruding and calen- dering. NBR 6240 is a low temperature polymerized polymer, and such as, retains the excellent physical and processing properties of a cold nitrile rubber. NBR 6240 is recommended to use in packings, shoe products, chemically blown sponge, oil field products, industrial and automotive molded parts.
Specification
Polymerization: Cold Emulsion
Bound AN Content(%): 34.0
Volatile Matter(%): 0.2
Ash(%): 0.3
Stabilizer : Non-Staining
Mooney Viscosity(ML1+4,100℃) : 41
Color: Light Tan
Specific Gravity: 0.99
Packaging Information
Bale Weight: 35kg
Storage Condition
Rubber should be stored in suitable condition such as no sunlight, no heat and dry place.
Recipes(ASTM D3187)
NBR 6240: 100.0 phr
HAF(IRB #7): 40.0
ZnO: 3.0
Stearic Acid: 1.0
TBBS: 0.7
Sulfur: 1.5
Total: 146.2
Stress-Strain Properties: (ASTM D412, 145℃×50min. Cured)
300% Modulus(kg/㎠): 128
Elongation(%): 594
Tensile (kg/㎠) : 308
*The above data is a typical value, therefore there may be a s light difference between the elements of a supplied product and the data.
- DAESAN PLANT : Tel 82-41-661-2114 FAX 82-41-661-2495
- R&D CENTER : Tel 82-41-661-2481 FAX 82-41-661-2495
- SEOUL OFFICE : Tel 82-2-398-6621 FAX 82-2-761-6573
- PUSAN OFFICE : Tel 82-51-801-2657 FAX 82-51-801-2650
NBR 6240 PACKING STUDY
Carbon Black(SRF) : 80.0
Zinc Oxide: 5.0
Stearic Acid: 1.0
Antioxidant(RD): 2.0
Antioxidant(3-C): 1.0
Plasticizer(DOP): 10.0
Sulfur: 0.5
TT: 1.0
CZ : 2.0
Total: 202.5
Rheometer(MDR,160℃×12 min,1˚Arc, MDR) ML(lb-in) 1.4
MH (lb-in): 23.6
ts1 (min.): 1.2
Tc'50 (min.) : 1.8
Tc'90 (min.): 2.8
|
Basic Properties(145℃×20min. Cured) Hardness(shore A) |
69 |
|
Elongation(%) |
400 |
|
Tensile (kg/㎠) |
187 |
|
Circulating Oven Aging(100℃×72hrs) Hardness Change(point) |
+4 |
|
Tensile Change(%) |
+5.6 |
|
Elongation Change(%) |
-26.8 |
|
Aged ASTM #1 Oil(100℃×72hrs) Hardness Change(point) |
+4 |
|
Tensile Change(%) |
+4.4 |
|
Elongation Change(%) |
-27.7 |
|
Volume Swell(%) |
-6.8 |
|
Aged ASTM #3 Oil(100℃×72hrs) Hardness Change(point) |
0 |
|
Tensile Change(%) |
+4.9 |
|
Elongation Change(%) |
-23.0 |
|
Volume Swell(%) |
-2.8 |
|
Aged FUEL C(R.T℃×72hrs) Hardness Change(point) |
-24 |
|
Tensile Change(%) |
-50.1 |
|
Elongation Change(%) |
-46.9 |
|
Volume Swell(%) |
+40.8 |
|
Compression Set(160℃×30min. Cured) 100℃×72hrs(%) |
21.1 |
|
Rebound(30℃, %) |
43.1 |
|
AKRON Abrasion |
0.2895 |
Hot Tags: nitrile butadiene rubber lg6240, China nitrile butadiene rubber lg6240 manufacturers, suppliers, factory, Nitrile Butadiene Rubber 3305E, Nitrile Butadiene Rubber 3308E, Nitrile Butadiene Rubber 3345, Nitrile Butadiene Rubber KNB35L, Nitrile Butadiene Rubber LG6240, Nitrile Butadiene Rubber LG6250